Title: In-situ investigations of hydrogen influenced crack initiation and propagation under tensile and low cycle fatigue loadings in RPV steel
Authors: Singh, R.
Singh, V.
Arora, A.
Mahajan, D. K.
Keywords: SA508 grade 3 class I low alloy steel
Tensile loading
Low cycle fatigue loading
Hydrogen charging
Crack initiation
Crack propagation
Issue Date: 28-Jul-2021
Abstract: Present work aims to unveil the mechanism of hydrogen embrittlement (HE) in SA508 Grade 3 Class I low alloy reactor pressure vessel (RPV) steel. In-situ tensile and low cycle fatigue (LCF) tests are performed on specially designed specimens using tensile/fatigue testing stage under scanning electron microscope (SEM). Electrochemical hydrogen charging resulted in localized void formation at prior austenite grain boundaries (PAGBs) during tensile loading. Alongside the hydrogen induced weakening of PAGBs due to synergetic HELP (hydrogen enhanced localized plasticity) and HEDE (hydrogen enhanced decohesion) mechanisms of HE, fish-eyes formation around Al2O3eSiO2 type inclusions are the primary factors for hydrogen enhanced tensile properties degradation in subject RPV steel. During LCF loading, crack initiation and propagation is facilitated by long rod inter-lath cementite particles distributed along the bainitic ferrite lath boundaries in the un-charged specimen. In case of hydrogen charged specimen, the edge crack formed during LCF loading propagated through the specimen by cleavage. Predominantly plasticity (slip) driven transgranular crack propagation occurred in un-charged specimen. In contrary, hydrogen charging resulted in LCF crack to propagate in mixed intergranular and transgranular manner during early stages of propagation, whereas once the crack length exceeded 5 to 6 grains, cleavage type transgranular crack propagation was observed.
URI: http://localhost:8080/xmlui/handle/123456789/2547
Appears in Collections:Year-2019

Files in This Item:
File Description SizeFormat 
Full Text.pdf8.33 MBAdobe PDFView/Open    Request a copy


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.