Title: On the nature of interface of carbon nanotube coated carbon fibers with different polymers
Authors: Bedi, H.S.
Padhee, S.S.
Agnihotri, P.K.
Issue Date: 19-Sep-2022
Abstract: Experimental investigations are carried out to analyse the wetting behaviour of carbon nanotube (CNT) coated carbon fiber to determine their suitability to process carbon nanotube coated carbon fiber/polymer multiscale composites for structural applications. To overcome the problem of agglomeration, CNTs are grown directly on the surface of carbon fibers as well as fabric using thermal chemical vapour deposition (CVD) technique. The term multiscale is used because different reinforcement mechanisms operate at the scale of long fibers and CNTs which are of few micrometers in length. The load carrying capacity of these multiscale composites critically depends on the efficiency and extent of load transfer from low strength matrix to high strength fiber which in turn depends on the interfacial strength between CNT coated carbon fiber and polymer matrix. A systematic analysis of wetting behaviour of CNT coated carbon fiber with epoxy and polyester matrix is carried out in this study. It is shown that CNT coated carbon fibers as well as fabric show better wettability with epoxy matrix as compared to polyester matrix. This results in stronger interface of CNT coated carbon fiber with epoxy as compared to polyester in multiscale composite system. A similar observation is made in nanoindentation testing of single fiber multiscale composites processed with epoxy and polyester matrix. In addition, it is observed that wettability, interfacial strength and average properties of CNT coated carbon fiber/polymer composites are a function of CNT density on the surface of carbon fibers.
URI: http://localhost:8080/xmlui/handle/123456789/4014
Appears in Collections:Year-2016

Files in This Item:
File Description SizeFormat 
Full Text.pdf1.55 MBAdobe PDFView/Open    Request a copy


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.