dc.description.abstractPresynthesized nanocrystalline Ni-20Cr powder was deposited on SA 516 and T91 boiler steels by a high-velocity oxy-fuel spraying process. Ni-20Cr powder was synthesized by the ball milling approach. The high-temperature oxidation behavior of bare and coated samples was then studied under cyclic isothermal conditions at 900 °C for 50 cycles. The kinetics of oxidation was established using weight change measurements for the bare and coated boiler steels. Uncoated and coated samples of T91 steel were exposed to the superheated zone of a power plant boiler at 750 °C under cyclic conditions for 15 cycles. Each cycle consisted of 100 h of heating followed by 1 h of cooling. Attempts were made to study the kinetics of erosion–corrosion using weight change and thickness loss data for the samples. Different characterization techniques were used to study the oxidized and eroded–corroded samples, including x-ray diffraction, scanning electron microscopy/energy-dispersive spectroscopy, and x-ray mapping analyses. The Ni-20Cr alloy powder coating was found to offer excellent oxidation resistance to the base steels and was successful in reducing the weight gain of SA 516 steel by 98.5 % and that of T91 steel by 65 %. The coating was observed to reduce the erosion–corrosion rate of T91 steel by 86 % in terms of thickness loss. This indicates that the investigated nanostructured coating can be a better choice over conventional coating for erosion–corrosion control of boiler tubes.en_US
dc.language.isoen_USen_US
dc.subjectBoiler steelsen_US
dc.subjectCoatingsen_US
dc.subjectErosion–corrosionen_US
dc.subjectHigh-temperature oxidationen_US
dc.subjectHVOFen_US
dc.subjectSprayingen_US
dc.subjectOxide scaleen_US
dc.titleProduction of nanocrystalline Ni-20Cr coatings for high-temperature applicationsen_US
dc.typeArticleen_US
Appears in Collections:Year-2014

Files in This Item:
File Description SizeFormat 
Full Text.pdf4.65 MBAdobe PDFView/Open    Request a copy


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.